PTFE gasket is manufactured by molding method with PTFE granular resin. Compared with other plastic, PTFE has a superior properties against chemicals and temperature. Because of such excellent properties, PTFE gasket has a wide application as a sealing material.
Technical Data Sheet
| Property | Unit | Result |
| Density | g/cm3 | 2.18 |
| Elongation at Break | % | 200~450 |
| Tensile Strength | Mpa | 14~18 |
| Bending Strength | Mpa | No Break |
| Pressure Resistance | Mpa | 24 |
| Tensile Modulus | Mpa | 393 |
| Bending Modulus | Mpa | 490~586 |
| Working Temperature
(20000 hr, highest) |
℃ |
260 |
Application Area
As a sealing material, PTFE gaskets can be used in flange joint of various equipments and pipes in chemical industry, food producing industry, medicine industry and so on. It can bear the most bitter chemical medium, and has good anti-creeping performance. The unloaded operating temperature range is -180~+260℃.
Product detail pictures:
Related Product Guide:
O-Ring Sizes for Industrial Applications
Useful Tips For Installing The Teflon Envelope Gasket
Top Suppliers PTFE Gasket Wholesale to Zimbabwe, The product will supply to all over the world, such as: , , ,
Toolfusion® 3 is a two part low viscosity epoxy infusion resin formulated to produce pre-preg quality, composite moulds. Toolfusion® 3 has a low initial cure temperature of 120ºF (49ºC) and can be post cured to achieve a high glass transition temperature of 425ºF (218ºC). Void contents of less than 1% are achievable. Toolfusion® 3 will work in various RTM and VARTM processes including single and double bag arrangements to produce autoclave quality laminates.
Benefits:
• Resin infusion process delivers very high quality laminates with low manufacturing costs, no refrigeration costs, no autoclave running costs.
• Low initial cure temperature for low thermal expansion effect during curing and ability to use low cost master model materials.
• Nano technology delivers outstanding toughness & high Tg. (218ºC) for long tool life and reduced life cycle cost.
• Low viscosity allows infusion of thicker and more complex laminates with fewer resin feed lines.
• In comparison to metallic tools, Toolfusion® 3 composite tools are lighter weight for easier manual handing.
• In comparison to metallic tooling, Toolfusion® 3 composite tools have faster heat up and cool down rates for reduced production costs.
• Toolfusion® 3 composite tooling laminates have vacuum integrity for vacuum bag processing of parts in oven and autoclave.
For more information, please visit: www.airtechonline.com
By from -
By from -